活性炭浸渍莫来石前驱体制备多孔陶瓷及其性能研究

doi:10.3969/j.issn.1001-1935.2025.05.008

耐火材料 ›› 2025, Vol. 59 ›› Issue (5): 413-421.DOI: 10.3969/j.issn.1001-1935.2025.05.008

活性炭浸渍莫来石前驱体制备多孔陶瓷及其性能研究

奚健飞¹⁾, 张玲¹⁾, 牛舒楠¹⁾, 罗式桐²⁾, 段明君²⁾

1)辽宁科技大学材料与冶金学院辽宁鞍山 114051
2)峰驰耐火材料有限公司辽宁海城 114200

收稿日期:2024-12-05 出版日期:2025-10-15 发布日期:2025-10-22
通讯作者: 张玲,女,1965年生,博士,教授。 E-mail:452433876@qq.com
作者简介:奚健飞:男,2000年生,硕士研究生。E-mail:17641243367@163.com
基金资助:
国家自然科学基金联合基金项目(U20A20239)。

Preparation of porous ceramics by impregnating mullite precursor with activated carbon and their perfor-mance

Xi Jianfei, Zhang Ling, Niu Shunan, Luo Shitong, Duan Mingjun

First author' s address:School of Materials and Metallurgy,University of Science and Technology Liao-ning,Anshan 114051,Liaoning,China

Received:2024-12-05 Online:2025-10-15 Published:2025-10-22

摘要/Abstract

摘要： 废弃活性炭的回收利用在环保方面具有重要意义。以十八水合硫酸铝、氨水及SiO₂微粉为原料,利用热处理后的废弃活性炭作为造孔剂,以聚丙烯酸钠(PASS)为分散剂,采用活性炭浸渍莫来石前驱体制备莫来石多孔陶瓷,研究了活性炭(添加质量分数分别为1.5%、3.0%、5.2%和7.8%)和PASS分散剂(外加质量分数分别为1%、2%和3%)对多孔陶瓷的物理性能、物相组成及显微结构的影响。结果表明:1)活性炭作为造孔剂促进了试样内部气孔的形成,并且随其加入量的增加,试样显气孔率显著提高;当活性炭加入量达到7.8%(w)时,试样的显气孔率达到65.7%,常温耐压强度为4.62 MPa,孔径峰值约为3.5 μm,孔径分布均匀。2)适量添加PAAS有助于改善活性炭在试样中的分散情况,提升多孔莫来石陶瓷的综合性能;当PAAS外加量为2%(w)时,试样的显气孔率为71.8%,常温耐压强度为5.53 MPa,孔径峰值约为3 μm,孔径分布得到优化;然而,过量添加PAAS会增加体系中的液相,导致莫来石过度烧结并使气孔率降低。

关键词: 废弃活性炭, 莫来石多孔陶瓷, 浸渍前驱体, 分散剂

Abstract: The recycling of waste activated carbon is of great significance in environmental protection.Porous mullite ceramics were prepared by impregnating the mullite precursor with activated carbon,and adopting aluminum sulfate octahydrate,ammonia and silica micropowder as raw materials,waste activated carbon after heat treatment as the pore forming agent,and sodium polyacrylate (PASS) as the dispersant.The effects of the activated carbon addition (1.5%,3.0%,5.2% and 7.8%,by mass) and PASS addition (1%,2% and 3%,extra adding,by mass) on the physical properties,phase composition and microstructure of the porous ceramics were studied.The results show that:(1)as a pore forming agent,activated carbon promotes the formation of pores inside the sample,while the apparent porosity of the samples increases significantly with the increasing activated carbon addition;when the activated carbon addition is 7.8%,the apparent porosity of the sample is 65.7%,the cold crushing strength is 4.62 MPa,the peak pore size is around 3.5 μm,and the pore size distribution is uniform;(2) appropriate PAAS helps to improve the dispersion of activated carbon in the samples and the comprehensive performance of the porous mullite ceramics;when the PAAS addition is 2%,the apparent porosity of the sample is 71.8%,the cold compressive strength is 5.53 MPa,the peak pore size is around 3 μm,and the pore size distribution is optimized;however,excessive PAAS increases the liquid phase in the system,resulting in over sintering of mullite and a decrease in the porosity.

Key words: waste activated carbon, porous mullite ceramics, impregnating precursor, dispersant

中图分类号:

TQ174

奚健飞, 张玲, 牛舒楠, 罗式桐, 段明君. 活性炭浸渍莫来石前驱体制备多孔陶瓷及其性能研究[J]. 耐火材料, 2025, 59(5): 413-421.

Xi Jianfei, Zhang Ling, Niu Shunan, Luo Shitong, Duan Mingjun. Preparation of porous ceramics by impregnating mullite precursor with activated carbon and their perfor-mance[J]. Refractories, 2025, 59(5): 413-421.

参考文献

[1] 李艳芳,孙仲超.国内外活性炭产业现状及我国活性炭产业的发展趋势[J].新材料产业,2012(11):4-9.
[2] JUETTNER T,MOERTEL H,SVINKA V,et al.Structure of kaoline-alumina based foam ceramics for high temperature applications[J]Journal of the European Ceramic Society,2007,27(2/3):1435-1441.
[3] 袁绮,谭划,杨廷旺,等.多孔陶瓷的制备方法及研究现状[J].硅酸盐通报,2021,40(8):2687-2701.
[4] SHE J H,OHJI T.Fabrication and characterization of highly porous mullite ceramics[J].Materials Chemistry and Physics,2003,80(3):610-614.
[5] DING S Q,ZENG Y P,JIANG D L.Fabrication of mullite ceramics with ultrahigh porosity by gel freeze drying[J].Journal of the American Ceramic Society,2007,90(7):2276-2279.
[6] QIAN H R,CHENG X D,ZHANG H P,et al.Preparation of porous mullite ceramics using fly ash cenosphere as a pore-forming agent by gelcasting process[J].International Journal of Applied Ceramic Technology,2014,11(5):858-863.
[7] CHOO T F,MOHD SALLEH M A,KOK K Y,et al.Modified cenospheres as non-sacrificial pore-forming agent for porous mullite ceramics[J].Ceramics International,2019,45(17):21827-21834.
[8] 熊洵,刘浩,马妍,等.多孔莫来石陶瓷制备与性能研究[J].耐火材料,2019,53(5):336-341+347.
[9] YAN X,YUAN L,LIU Z,et al.Preparation of porous mullite ceramic for high temperature flue gas filtration application by gel casting method[J].Journal of the Australian Ceramic Society,2021,57(4):1189-1198.
[10] 李红霞.双碳背景下耐火材料科技创新的思考[J].耐火材料,2021,55(5):381-384.
[11] 王宝林.高强度莫来石泡沫陶瓷的制备[D].鞍山:辽宁科技大学,2022.
[12] 李洪泉.关于比强度和比模量单位的使用辨析[J].宇航材料工艺,2012,42:112.
[13] SARUHAN B,ALBERS W,SCHNEIDER H,et al.Reaction and sintering mechanisms of mullite in the systems cristobalite/α-Al₂O₃ and amorphous SiO₂/α-Al₂O₃[J].Journal of the European Ceramic Society,1996,16(10):1075-1081.
[14] YAN K Z,GUO Y X,LIU D D,et al.Thermal decomposition and transformation mechanism of mullite with the action of sodium carbonate[J].Journal of Solid State Chemistry,2018,265:326-331.
[15] PROSKURNINA N V,VORONIN V I,SHEKHTMAN G S,et al.Crystal structure of NaFeO₂ and NaAlO₂ and their correlation with ionic conductivity[J].Ionics,2020,26(6):2917-2926.
[16] WISNIEWSKA M,NOSAL-WIERCINSKA A,OSTOLSKA I,et al.Nanostructure of poly(Acrylic Acid) adsorption layer on the surface of activated carbon obtained from residue after supercritical extraction of hops[J].Nanoscale Res Lett,2017,12(1):2.
[17] 郭童双,邓承继,祝洪喜,等.耐火材料的气孔特性与物理性能相关性的研究进展[J].陶瓷学报,2018,39(3):265-271.
[18] 谭宏斌.用硅灰低温制备莫来石晶须[J].机械工程材料,2012,36(1):35-36+40.
[19] 谭宏斌,马小玲.钠对莫来石纤维形貌的影响研究[J].中国陶瓷,2013,49(1):43-44.
[20] MIYAZAKI N,HOSHIDE T.Influence of porosity and pore distributions on strength properties of porous alumina[J].Journal of Materials Engineering and Performance,2018,27(8):4345-4354.

活性炭浸渍莫来石前驱体制备多孔陶瓷及其性能研究

Preparation of porous ceramics by impregnating mullite precursor with activated carbon and their perfor-mance

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	孙易桀, 马妍, 王周福, 刘浩, 何健, 吕戌生, 王玺堂. 氧化温度和分散剂种类对Si₃N₄浆料性能的影响[J]. 耐火材料, 2022, 56(1): 24-28.
[2]	石颖恒, 王超, 员文杰. 氧化铝微粉的特性和分散剂对浆料流变特性的影响[J]. 耐火材料, 2021, 55(1): 21-25.
[3]	张冰冰,朱伯铨,李享成,陈平安. 不同分散剂对磷酸结合刚玉质浇注料基质浆体流变性能的影响[J]. , 2019, 53(6): 423-429.
[4]	徐晗1）,刘源2）,徐恩霞1）,王长春2）,刘豪2）. 分散剂和pH对水基SiC-Si料浆流变性和Zeta电位的影响[J]. , 2019, 53(1): 31-33.
[5]	王庆恒,李远兵,魏昊,徐娜娜,李淑静. 分散剂及氧化铝微粉对钢包用Al2O3-MgO浇注料施工性能的影响[J]. , 2018, 52(4): 288-291.
[6]	吴彤1) ,叶建东2). 超分散剂在制备α- Al2O3悬浮浆料中的应用研究[J]. , 2018, 52(4): 292-295.
[7]	李赛赛,梁峰,李发亮,王军凯,宋健波,张海军. 葡萄糖水热炭化制备单分散炭微球的工艺优化研究[J]. , 2017, 51(1): 32-36.
[8]	康峰刘开琪罗志勇袁永兵. 微米级α-Al2O3悬浮液的制备[J]. , 2015, 49(5): 361-364.
[9]	姜欣1）,李泉2）,张宏浩2）,王刚1）,刘国齐1）,付建莹1）. 颗粒级配和分散剂对ZrO2浆料流变性能的影响[J]. , 2014, 48(4): 269-271.
[10]	李再耕. 耐火浇注料用分散剂进展[J]. , 2010, 44(2): 144-0.
[11]	王锋刚1，2）朱伯铨2）李天清1）贺中央1）. 分散剂对含Al2O3凝胶粉的Al2O3-MgO质浆料流变特性的影响[J]. , 2009, 43(1): 16-0.
[12]	许远超2),王战民1)2),曹喜营1)2),洪彦若1),王金相2),李再耕2). α-Al2O3微粉和SiO2微粉浆体的动电特性和流变行为研究[J]. , 2008, 42(3): 175-0.
[13]	王峰姚金甫. 分散剂对Al2O3微粉-水和SiO2微粉-水体系性能的影响[J]. , 2006, 40(6): 453-0.
[14]	封鉴秋, 杜光旭, 贾晓林, 李素平. 刚玉质自流渗浆浇注料浆体的流变特性 [J]. , 2006, 40(5): 335-338.
[15]	张欣, 申少华, 刘俊成, 谢玉华 . 铝硅质低水泥浇注料的研制 [J]. , 2005, 39(5): 354-356.