Al/Si复合粉包覆改性刚玉颗粒对Al2O3-C材料性能的影响

doi:10.3969/j.issn.1001-1935.2023.02.014

耐火材料 ›› 2023, Vol. 57 ›› Issue (2): 153-156.DOI: 10.3969/j.issn.1001-1935.2023.02.014

Al/Si复合粉包覆改性刚玉颗粒对Al₂O₃-C材料性能的影响

刘洋¹⁾, 刘宝亮²⁾, 石凯¹⁾, 马世行¹⁾, 商剑钊¹⁾, 夏熠¹⁾

1)河南工业大学材料科学与工程学院河南郑州 450001
2)河南省工业学校河南郑州 450011

收稿日期:2022-05-16 出版日期:2023-04-15 发布日期:2023-04-17
作者简介:刘洋:男,1996年生,硕士研究生。E-mail:2421526715@qq.com
基金资助:
河南省科技厅科技研发专项(212102210579)。

Effect of Al/Si composite powder coating modified corundum particles on properties of Al₂O₃-C materials

Liu Yang, Liu Baoliang, Shi Kai, Ma Shihang, Shang Jianzhao, Xia Yi

First author’s address: School of Materials Science and Engineering, Henan University of Technology, Zhengzhou 450001, Henan, China

Received:2022-05-16 Online:2023-04-15 Published:2023-04-17

摘要/Abstract

摘要： 首先,以3~1 mm的板状刚玉颗粒,Al粉、Si粉质量比分别为4∶0、3∶1、2∶2的Al/Si复合粉,以及酚醛树脂-乙二醇混合液为原料,通过搅拌、180 ℃烘烤、解体制成Al/Si复合粉包覆改性板状刚玉颗粒。然后,按常规工艺制备Al₂O₃-C试样,检测试样的常温和高温性能,分析试样的物相组成和显微结构。结果表明:1)在Al₂O₃-C材料中加入Al/Si复合粉包覆改性刚玉颗粒,可提高材料的致密度、常温强度、高温强度、抗热震性和抗氧化性;Al/Si复合粉中Al粉、Si粉的质量比以3∶1最佳。2)改性板状刚玉颗粒表面的Al粉和Si粉填充在颗粒表面的凹陷处,提高了试样的成型致密度以及烘烤后和埋炭热处理后试样的致密度、强度和抗氧化性;高温埋炭热处理后,这些Al粉和Si粉反应生成AlN、Al₄C₃、SiC等非氧化物,增强了改性刚玉颗粒与基质的结合,提高了试样的抗热震性和强度。

关键词: Al₂O₃-C材料, 包覆改性, 刚玉颗粒, 非氧化物, 结合强度

Abstract: First,Al/Si composite powder coating modified corundum particles were prepared using tabular corundum particles (1-3 mm),Al/Si composite powder (mass ratio of Al powder to Si powder=4∶0,3∶1 or 2∶2),and phenolic resin-ethylene glycol mixed solution as raw materials,stirring,baking at 180 ℃ and disintegrating.Then,Al₂O₃-C samples were prepared according to the conventional process.The cold and hot properties of the samples were tested.The phase composition and the microstructure were analyzed.The results show that:(1)adding Al/Si composite powder coating modified corundum particles into Al₂O₃-C samples can improve their density,cold and hot strengths,thermal shock resistance and oxidation resistance;the Al/Si composite powder with the mass ratio of Al powder to Si powder of 3∶1 is the optimum;(2)the Al powder and the Si powder fill in the depressions on the surface of the modified tabular corundum particles,which improves the forming density of the samples as well as the density,the strength and the oxidation resistance of the samples after baking and carbon embedded heat treatment;after high temperature carbon embedded heat treatment,the Al powder and the Si powder react to form non-oxides such as AlN,Al₄C₃ and SiC,which enhance the bonding of the modified corundum particles and the matrix,thus improving the thermal shock resistance and the strength of the samples.

Key words: alumina-carbon materials, coating modification, corundum particles, non-oxides, bonding strength

中图分类号:

TQ175

刘洋, 刘宝亮, 石凯, 马世行, 商剑钊, 夏熠. Al/Si复合粉包覆改性刚玉颗粒对Al₂O₃-C材料性能的影响[J]. 耐火材料, 2023, 57(2): 153-156.

Liu Yang, Liu Baoliang, Shi Kai, Ma Shihang, Shang Jianzhao, Xia Yi. Effect of Al/Si composite powder coating modified corundum particles on properties of Al₂O₃-C materials[J]. Refractories, 2023, 57(2): 153-156.

[1]	张婧, 王子昊, 凌永一, 王珍, 徐恩霞, 贾全利, 刘新红. Mg粉对Al₂O₃-C滑板材料性能的影响[J]. 耐火材料, 2022, 56(2): 137-140.
[2]	闫明伟, 杨裕民, 仝尚好, 张佳钰, 孙广超, 刘开琪. 高温氮气下镁碳耐火材料的物相重构与微结构演变[J]. 耐火材料, 2022, 56(2): 93-100.
[3]	杜鹏辉1),于仁红2),周宁生2),王刚1),韩建燊1). 添加Si粉 - 埋碳热处理对刚玉浇注料性能的影响[J]. , 2019, 53(6): 445-447.
[4]	孟红涛1,2),郝明选1),王允2),方文吉2). 换热式两段焦炉用SiC换热器的研制及应用[J]. , 2019, 53(5): 380-383.
[5]	曾渊,刘江昊,梁峰,谭操,张海军. 石墨烯增强增韧非氧化物陶瓷的研究进展[J]. , 2019, 53(1): 76-80.
[6]	陈晓雨,文钰斌,陈浩,顾强,刘新红,贾全利. 易氧化材料的应力-氧化研究进展[J]. , 2018, 52(1): 75-80.
[7]	韩磊，邓先功,王军凯,梁峰, 张海军. SiC复相多孔陶瓷的研究进展[J]. , 2017, 51(3): 227-234.
[8]	宋健波,张海军,王军凯,张少伟. 碳纳米管增强陶瓷基复合材料的研究现状[J]. , 2017, 51(2): 152-156.
[9]	尹月,马北越,张博文,李世明,于景坤. 非氧化物多孔陶瓷的研究进展[J]. , 2016, 50(3): 233-240.
[10]	黄仲1) ,焦成鹏1, 2) ,张少伟1),张海军1),李发亮1) ,鲁礼林1). 熔盐法合成非氧化物陶瓷粉体[J]. , 2015, 49(3): 232-237.
[11]	任桢,马成良,钟香崇. 热处理温度对Al复合低碳MgO-C材料组成和结构的影响[J]. , 2015, 49(2): 81-85.
[12]	曹迎楠,杜爽,张海军,张少伟,张振聪. 溶胶-凝胶工艺制备非氧化物超细粉体的研究现状[J]. , 2014, 48(4): 302-306.
[13]	张艳利1）谢朝晖2）李志刚1）贾全利3）. 复合型耐火原料的研究进展[J]. , 2013, 47(4): 298-302.
[14]	贾全利，吴然，孙小改. 精炼钢包用透气砖的研究进展与发展方向[J]. , 2013, 47(1): 58-60.
[15]	刘新红，钟香崇. 加入不同量Al粉和Si粉的低碳Al2O3-C滑板的高温力学性能[J]. , 2013, 47(1): 6-9.

Al/Si复合粉包覆改性刚玉颗粒对Al₂O₃-C材料性能的影响

Effect of Al/Si composite powder coating modified corundum particles on properties of Al₂O₃-C materials

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价