原料特性对镁铝尖晶石烧结致密化影响的研究进展

doi:10.3969/j.issn.1001-1935.2023.03.016

耐火材料 ›› 2023, Vol. 57 ›› Issue (3): 259-264.DOI: 10.3969/j.issn.1001-1935.2023.03.016

原料特性对镁铝尖晶石烧结致密化影响的研究进展

王建斌, 王战民, 冯海霞, 柳军, 韩艺辉, 潘元帅

中钢集团洛阳耐火材料研究院有限公司先进耐火材料国家重点实验室河南洛阳 471039

收稿日期:2022-07-23 出版日期:2023-06-15 发布日期:2023-06-21
通讯作者: 王战民,男,1966年生,博士,正高级工程师。E-mail:wangzm@lirrc.com
作者简介:王建斌:男,1998年生,硕士研究生。E-mail:918670736@qq.com

Research progress on effect of raw material characteristics on sintering densification of magnesium aluminate spinel

Wang Jianbin, Wang Zhanmin, Feng Haixia, Liu Jun, Han Yihui, Pan Yuanshuai

First author’s address: State Key Laboratory of Advanced Refractories, Sinosteel Luoyang Institute of Refractories Research Co., Ltd., Luoyang 471039, Henan, China

Received:2022-07-23 Online:2023-06-15 Published:2023-06-21

摘要/Abstract

摘要： 根据原料不同的性质以及影响镁铝尖晶石致密化的烧结机制,分别从原料种类、化学组成、粒度分布、预处理等方面综述了原料特性对镁铝尖晶石烧结致密化的影响,指出今后的研究重点在于如何量化镁铝尖晶石原料性质与制备材料性能之间的关系,实现原料的低温无压烧结,以利于工业制造过程中,在满足使用性能的要求下进一步节能降耗和环境友好。

关键词: 原料特性, 镁铝尖晶石, 烧结致密化, 精密器件, 耐火材料

Abstract: According to the different properties of raw materials and the sintering mechanism affecting the densification of magnesium aluminate spinel,the effects of raw material characteristics on the sintering densification of magnesium aluminate spinel were reviewed from the aspects of the raw material type,chemical composition,particle size distribution and pretreatment.It was pointed out that the future research focus is how to quantify the relationship between the properties of magnesium aluminate spinel raw materials and the properties of prepared materials,so as to realize the low-temperature pressureless sintering of raw materials,which is conducive to further energy saving and environmental friendliness with the satisfied performance in the industrial manufacturing process.

Key words: raw material characteristics, magnesium aluminate spinel, sintering densification, precision devices, refractories

中图分类号:

王建斌, 王战民, 冯海霞, 柳军, 韩艺辉, 潘元帅. 原料特性对镁铝尖晶石烧结致密化影响的研究进展[J]. 耐火材料, 2023, 57(3): 259-264.

Wang Jianbin, Wang Zhanmin, Feng Haixia, Liu Jun, Han Yihui, Pan Yuanshuai. Research progress on effect of raw material characteristics on sintering densification of magnesium aluminate spinel[J]. Refractories, 2023, 57(3): 259-264.

参考文献

[1] RUBAT DU MERAC M,KLEEBE H J,MÜLLER M M,et al.Fifty years of research and development coming to fruition;unraveling the complex interactions during processing of transparent magnesium aluminate (MgAl₂O₄) spinel[J].Journal of the American Ceramic Society,2013,96(11):3341-3365.
[2] GANESH I.A review on magnesium aluminate (MgAl₂O₄) spinel:synthesis,processing and applications[J].International Materials Reviews,2013,58(2):63-112.
[3] GOLDSTEIN A.Correlation between MgAl₂O₄-spinel structure,processing factors and functional properties of transparent parts (progress review)[J].Journal of the European Ceramic Society,2012,32(11):2869-2886.
[4] SAKO E Y,BRAULIO M A L,ZINNGREBE E,et al.Fundamentals and applications on in situ spinel formation mechanisms in Al₂O₃-MgO refractory castables[J].Ceramics International,2012,38(3):2243-2251.
[5] TABAZA W A I,SWART H C,KROON R E.Luminescence of Ce doped MgAl₂O₄ prepared by the combustion method[J].Physica B:Physics of Condensed Matter,2014,439:109-114.
[6] GOLDSTEIN A,LOIKO P,BURSHTEIN Z,et al.Development of saturable absorbers for laser passive q-switching near 1.5 μm based on transparent ceramic Co²⁺:MgAl₂O₄[J].Journal of the American Ceramic Society,2016,99(4):1324-1331.
[7] 荆桂花,肖国庆.镁铝尖晶石基耐火材料的最新研究进展[J].耐火材料,2004,38(5):347-349.
[8] OBRADOVIC N,FILIPOVIC S,DORDEVIC N,et al.Effects of mechanical activation and two-step sintering on the structure and electrical properties of cordierite-based ceramics[J].Ceramics International,2016,42(12):13909-13918.
[9] SARKAR R,DAS S K,BANERJEE G.Calcination effect on magnesium hydroxide and aluminium hydroxide for the development of magnesium aluminate spinel[J].Ceramics International,2000,26(1):25-28.
[10] MORA A,GUTIÉRREZ-CAMPOS D,LAVELLE C,et al.Evaluation of bayer process gibbsite reactivity in magnesium aluminate spinel formation[J].Materials Science & Engineering:A,2006,454:139-143.
[11] 刘江波,王周福,王敬伟,等.不同氧化铝源对富镁尖晶石烧结行为的影响[J].机械工程材料,2017,41(2):20-23.
[12] SARKAR R,MUKHERJEE S,GHOSH A.Effect of AIF₃ on spinel formation[J].Industrial Ceramics,2008,28(1):33-36.
[13] GANESH I,TEJA K A,THIYAGARAJAN N, et al.Formation and densification behavior of magnesium aluminate spinel:the influence of CaO and moisture in the precursors[J].Journal of the American Ceramic Society,2005,88(10):2752-2761.
[14] MOHAMMADI F,OTROJ S,NILFORUSHAN M R.Effect of MgCl₂ addition on the sintering behavior of MgAl₂O₄ spinel and formation of nano-particles[J].Science of Sintering,2014,46(2):157-168.
[15] SARKAR R,PAL T K,BANERJEE G.Reaction sintering of magnesium aluminates:effect of MgSO₄[J].American Ceramic Society Bulletin,2003,82(8):9601-9607.
[16] MOHAN S K,SARKAR R.Effect of in situ generated nascent magnesia and alumina from nitrate precursor on reaction sintered magnesium aluminate spinel[J].Materials & Design,2016,110:145-156.
[17] ZHANG Z H,LI N.Effect of polymorphism of Al₂O₃ on the synthesis of magnesium aluminate spinel[J].Ceramics International,2004,31(4):583-589.
[18] HAN D,ZHANG J,LIU P,et al.Effect of polymorphism of Al₂O₃ on the sintering and microstructure of transparent MgAl₂O₄ ceramics[J].Optical Materials,2017,71:62-65.
[19] SEKO A,YUGE K,OBA F,et al.First-principles study of cation disordering in MgAl₂O₄ spinel with cluster expansion and Monte Carlo simulation[J].Physical Review B,2006,73(9):4116-1+6.
[20] WU G P,WANG J,DING W,et al.A strategy to promote the electrocatalytic activity of spinels for oxygen reduction by structure reversal[J].Angewandte Chemie International Edition,2016,55(4):1340-1344.
[21] TALIMIAN A,POUCHLY V,EL-MAGHRABY F H,et al.Impact of high energy ball milling on densification behaviour of magnesium aluminate spinel evaluated by master sintering curve and constant rate of heating approach[J].Ceramics International,2019,45(17):23467-23474.
[22] 曹晓炜,易帅,曾春燕,等.两种镁源反应烧结合成镁铝尖晶石[J].耐火材料,2013,47(2):104-106,110.
[23] SINHAMAHAPATRA S,TRIPATHI H S,GHOSH A.Densification and properties of magnesia-rich magnesium-aluminate spinel derived from natural and synthetic raw materials[J].Ceramics International,2016,42(4):5148-5152.
[24] 玄松桐,田玉明,王晓军.Al₂O₃/MgO比例对合成尖晶石陶瓷材料性能的影响[J].材料科学与工程学报,2022,40(4):652-656+724.
[25] SARKAR R,SAHOO S.Effect of raw materials on formation and densification of magnesium aluminate spinel[J].Ceramics International,2014,40(10):16719-16725.
[26] ZHOU Y,YE D C,WU Y Q,et al.Low-cost preparation and characterization of MgAl₂O₄ ceramics[J].Ceramics International,2022,48(5):7316-7319.
[27] ŁODZIANA Z,PIECHOTA J.Ab initio thermodynamic properties of point defects and O-vacancy diffusion in Mg spinels[J].Physical Review B,2006,74(18):184117.
[28] TEEVAN J.The effect of titanium dioxide doping on the grain growth and grain-boundary energy of magnesium aluminate spinel[D].Bethlehem:Lehigh University,2010.
[29] RUBAT DU MERAC M,REIMANIS I E,SMITH C,et al.Effect of impurities and LiF additive in hot-pressed transparent magnesium aluminate spinel[J].International Journal of Applied Ceramic Technology,2012,10:E33-E48.
[30] JONO K,MORI J,TORITANI Y.Effect of alumina grain size on spinel formation[J].Taikabutsu overseas,1996,16(3):12-16.
[31] TRIPATHI H S,GHOSH A.Spinelisation and properties of Al₂O₃-MgAl₂O₄-C refractory:Effect of MgO and Al₂O₃ reactants[J].Ceramics International,2010,36(4):1189-1192.
[32] BRAULIO M A L,BITTENCOURT L R M,PANDOLFELLI V C.Magnesia grain size effect on in situ spinel refractory castables[J].Journal of the European Ceramic Society,2008,28(15):2845-2852.
[33] BRAULIO M A L,BRANT P O C,BITTENCOURT L R M,et al.Microsilica or MgO grain size:Which one mostly affects the in situ spinel refractory castable expansion?[J].Ceramics International,2009,35(8):3327-3334.
[34] BRAULIO M A L,CASTRO J F R,PAGLIOSA C,et al.From macro to nanomagnesia:designing the in situ spinel expansion[J].Journal of the American Ceramic Society,2008,91(9):3090-3093.
[35] DUNCAN F C,BRADT R C.Reactant size effects on MgAl₂O₄ formation expansion[C]//Proceedings of the Unified International Technical Conference on Refractories (UNITECR 2013),Victoria,Canada,2013:233-238.
[36] KRELL A,HUTZLER T,KLIMKE J,et al.Fine‐grained transparent spinel windows by the processing of different nanopowders[J].Journal of the American Ceramic Society,2010,93(9):2656-2666.
[37] SARKAR R,GHOSH A,DAS S K.Reaction sintered magnesia rich magnesium aluminate spinel:effect of alumina reactivity[J].Ceramics International,2003,29(4):407-411.
[38] SARKAR R,CHATTERJEE S,MUKHERJEE B, et al.Effect of alumina reactivity on the densification of reaction sintered nonstoichiometric spinels[J].Ceramics International,2003,29(2):195-198.
[39] TRIPATHI H S,MUKHERJEE B,DAS S,et al.Synthesis and densification of magnesium aluminate spinel:effect of MgO reactivity[J].Ceramics International,2003,29(8):915-918.
[40] 彭强,郭玉香,曲殿利,等.轻烧MgO的活性对合成镁铝尖晶石晶体结构及性能的影响[J].人工晶体学报,2017,46(10):1913-1917.
[41] BAILEY J T.Sintered spinel ceramics[J].American Ceramic Society Bulletin,1968,47(11):1025-1029.
[42] GANESH I,OLHERO S M,REBELO A H,et al.Formation and densification behavior of MgAl₂O₄ spinel:the influence of processing parameters[J].Journal of the American Ceramic Society,2008,91(6):1905-1911.
[43] SUN X,JIANG X,SHAN Y,et al.Low-temperature solid reaction synthesis of high sinterability MgAl₂O₄ powder from γ-Al₂O₃+MgO and θ/α-Al₂O₃+MgO batches[J].Ceramics International,2022,48(12):17471-17480.
[44] TING J M,LIN R Y.Effect of particle-size distribution on sintering:Part Ⅰ Modelling[J].Journal of Materials Science,1994,29(7):1867-1872.
[45] MA J,LIM L C.Effect of particle size distribution on sintering of agglomerate-free submicron alumina powder compacts[J].Journal of the European Ceramic Society,2002,22(13):2197-2208.
[46] CHIANG Y.Grain boundary mobility and segregation in non-stoichiometric solid solutions of magnesium aluminate spinel[D].Cambridge:Massachusetts Institute of Technology,1985.
[47] 陈庆洁,周俊虎,管锡萍,等.化学组成对轻烧镁铝尖晶石结构与性能的影响[J].硅酸盐通报,2021,40(4):1388-1394.
[48] 范沐旭,石干,张伟.不同 Al₂O₃ 含量镁铝尖晶石材料高温力学性能研究[J].耐火材料,2021,55(1):35-39.
[49] OKUYAMA Y,KURITA N,FUKATSU N.Defect structure of alumina-rich nonstoichiometric magnesium aluminate spinel[J].Solid State Ionics,2005,177(1/2):59-64.
[50] BENAMEUR N,BERNARD-GRANGER G,ADDAD A,et al.Sintering analysis of a fine-grained alumina-magnesia spinel powder[J].Journal of the American Ceramic Society,2011,94(5):1388-1396.
[51] SPUSTA T,SVOBODA J,MACA K.Study of pore closure during pressure-less sintering of advanced oxide ceramics[J].Acta Materialia,2016,115:347-353.
[52] 罗皓鸣,韩丹,章健,等.粉体酸洗对镁铝尖晶石透明陶瓷性能的影响[J].陶瓷学报,2022,43(3):433-440.
[53] ZYCH Ł,LACH R,WAJLER A.The influence of the agglomeration state of nanometric MgAl₂O₄ powders on their consolidation and sintering[J].Ceramics International,2014,40(7):9783-9790.

原料特性对镁铝尖晶石烧结致密化影响的研究进展

Research progress on effect of raw material characteristics on sintering densification of magnesium aluminate spinel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	姚路炎, 韩兵强, 张锦化, 柯昌明. Ti-Si-Fe合金添加量对Si₃N₄结合SiC材料结构与性能的影响[J]. 耐火材料, 2024, 58(4): 277-283.
[2]	高云琴, 郭凯歌, 马爱琼, 牛兴荣, 杨光, 张旭东. 莫来石-刚玉-镁铝尖晶石复相材料的抗碱侵蚀性能研究[J]. 耐火材料, 2024, 58(4): 334-340.
[3]	梁效诚, 冯雨, 刘中飞, 罗旭东, 黄敏, 吴锋. 预合成CaZrO₃对镁锆质耐火材料性能的影响[J]. 耐火材料, 2024, 58(3): 213-217.
[4]	矫长发, 李国华, 孙格格, 田琳, 康驰. 发泡-自发凝固浇注法制备镁铝尖晶石质多孔材料[J]. 耐火材料, 2024, 58(3): 224-229.
[5]	刘然, 刘晏廷, 高艳甲, 邓勇. 熔融还原炼铁工艺用耐火材料的研究进展[J]. 耐火材料, 2024, 58(3): 251-256.
[6]	陈天任, 王战民, 秦红彬, 梁成凯, 李旭治. 氢冶金工艺及氢基竖炉用耐火材料研究进展[J]. 耐火材料, 2024, 58(3): 263-269.
[7]	矫长发, 李国华, 孙格格, 田琳, 康驰. 羧甲基纤维素钠加入量对镁铝尖晶石质多孔隔热材料性能的影响[J]. 耐火材料, 2024, 58(2): 122-126.
[8]	慕鑫, 贾毅, 刘春阳, 柴光伟, 余吴明, 杜传明, 马北越. 废旧高铝砖在LF精炼渣中的溶解行为研究[J]. 耐火材料, 2024, 58(1): 25-29.
[9]	徐国涛, 王志强, 秦世民, 刘黎, 张洪雷, 张彦文, 周旺枝. 新一代六铝酸钙质浇注料的研制与应用[J]. 耐火材料, 2024, 58(1): 53-56.
[10]	张巍, 王京阳. 莫来石复合耐火材料的应用进展[J]. 耐火材料, 2024, 58(1): 80-86.
[11]	李斌, 刘杰, 朱波, 郭玉涛, 任博, 封吉圣, 陈俊红. CA₆质耐火材料在水泥回转窑过渡带的应用及损毁机制[J]. 耐火材料, 2023, 57(6): 479-483.
[12]	王明刚, 车连房, 史成龙, 袁宏伟, 刘永振. 钛白粉回转窑用耐火材料的配置及应用[J]. 耐火材料, 2023, 57(6): 504-507.
[13]	丁嘉辉, 张利新, 邓俊杰, 刘萍, 徐恩霞, 李素平. 危废处理焚烧炉内衬用耐火材料研究进展[J]. 耐火材料, 2023, 57(6): 538-541.
[14]	余吴明, 慕鑫, 杜传明, 马北越, 于景坤. 废旧耐火材料用作钢铁冶金熔剂的研究进展[J]. 耐火材料, 2023, 57(6): 542-545.
[15]	李红霞. 先进耐火材料创新助推国家战略实施[J]. 耐火材料, 2023, 57(5): 369-376.