以微孔刚玉-尖晶石骨料替代刚玉骨料制备刚玉-尖晶石浇注料

doi:10.3969/j.issn.1001-1935.2023.06.011

耐火材料 ›› 2023, Vol. 57 ›› Issue (6): 514-517.DOI: 10.3969/j.issn.1001-1935.2023.06.011

以微孔刚玉-尖晶石骨料替代刚玉骨料制备刚玉-尖晶石浇注料

刘学新^{1, 2)}, 张锦化¹⁾, 陈鑫铭¹⁾, 王景然¹⁾, 杨宗源¹⁾, 韩兵强¹⁾, 柯昌明¹⁾

1)武汉科技大学省部共建耐火材料与冶金国家重点实验室湖北武汉 430081
2)湖北斯曼新材料股份有限公司湖北黄冈 438400

收稿日期:2023-03-24 发布日期:2023-12-25
通讯作者: 柯昌明,男,1955年生,博士,教授。 E-mail: kechangming@wust.edu.cn
作者简介:刘学新:男,1976年生,博士研究生。E-mail:lxx@hbsmile.cn
基金资助:
唐山市科技计划(19140207F)。

Preparation of corundum-spinel castables using microporous corundum-spinel aggregates to replace corundum aggregates

Liu Xuexin, Zhang Jinhua, Chen Xinming, Wang Jingran, Yang Zongyuan, Han Bingqiang, Ke Changming

First author's address: The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology,Wuhan 430081,Hubei,China

Received:2023-03-24 Published:2023-12-25

摘要/Abstract

摘要： 为提高钢包工作衬用刚玉-尖晶石浇注料的保温性能,以微孔刚玉-尖晶石骨料部分或全部替代同粒级的烧结刚玉骨料,制备了刚玉-尖晶石浇注料,对比研究了不同骨料对浇注料的体积密度、气孔率、力学强度、热导率、抗渣性等的影响。结果表明:采用微孔刚玉-尖晶石骨料部分或全部替代同粒级的烧结刚玉骨料制备的刚玉-尖晶石浇注料,其体积密度和热导率均明显降低,抗渣性能与传统烧结刚玉骨料制备的浇注料相当。将其用于钢包工作衬,有助于钢包减重,提高钢包保温性能。

关键词: 微孔骨料, 刚玉-尖晶石, 钢包浇注料, 热导率, 抗渣性能

Abstract: To improve the thermal insulation properties of corundum-spinel castables for the steel ladle working lining,the castables were prepared using microporous corundum-spinel aggregates to partially or totally replace sintered corundum aggregates with the same grain size.Effects of the aggregates on the bulk density,porosity,mechanical strength,thermal conductivity and slag resistance were investigated.The results indicate that,when the sintered corundum aggregates were substituted by microporous corundum-spinel aggregates partially or totally with the same grain size,the bulk density and thermal conductivity decrease remarkably,and the slag resistance is similar.As the working lining,the developed castables are beneficial to reducing the ladle mass and improving ladle insulation performance.

Key words: microporous aggregate, corundum-spinel, steel ladle castables, thermal conductivity, slag resistance

中图分类号:

TQ175

刘学新, 张锦化, 陈鑫铭, 王景然, 杨宗源, 韩兵强, 柯昌明. 以微孔刚玉-尖晶石骨料替代刚玉骨料制备刚玉-尖晶石浇注料[J]. 耐火材料, 2023, 57(6): 514-517.

Liu Xuexin, Zhang Jinhua, Chen Xinming, Wang Jingran, Yang Zongyuan, Han Bingqiang, Ke Changming. Preparation of corundum-spinel castables using microporous corundum-spinel aggregates to replace corundum aggregates[J]. Refractories, 2023, 57(6): 514-517.

参考文献

[1] 邱文冬,牟济宁,陈金荣,等.宝钢300 t钢包用国产浇注料的性能与应用[J].耐火材料,2001,35(6):331-333.
[2] BRAULIO M A L,RIGAUD M,BUHR A,et al.Spinel-containing alumina-based refractory castables[J].Ceramics International,2011,37(6):1705-1724.
[3] 黄传,倪月娥,柯昌明,等.氢氧化镁粒度对刚玉-尖晶石材料结构与性能的影响[J].耐火材料,2021,55(4):305-308.
[4] 付绿平,顾华志,黄奥,等.低导热微孔刚玉骨料的湿法制备及其抗渣机制研究[J].耐火材料,2015, 49(6):406-411.
[5] 富谷尚士,淹泽倫顕,多田秀德.取锅用Al₂O₃-MgO-Cれんがの低热伝導化[J].耐火物,2010,62(1):34-35.
[6] 西村雅史,佐々木久晴,難波誠.取鍋用流し込み材の軽量化についての検討[J].耐火物,2010,62(1):28-29.
[7] GU H Z,FU L P,MA L Y,et al.Preparation of microporous corundum aggregates and their applications in lightweight alumina-magnesia castables[J].Interceram-International Ceramic Review,2014,63(3):121-124.
[8] 彭从华,李楠,韩兵强.微孔刚玉和板状刚玉耐火材料的抗渣性对比[J].耐火材料,2008,42(6):448-450.
[9] 顾华志,付绿平,黄奥,等.轻量化耐火材料的研制与应用[J].耐火材料,2021,55(4):309-315.
[10] 柯昌明,张锦化,王景然,等.一种梯度组成微孔刚玉-尖晶石材料及其制备方法:CN108409308B[P].2021-06-04.
[11] LIU X X,ZHANG J H,WANG J R,et al.Corrosion of chemical-mineralogical gradient submicron-porous Al₂O₃-MgAl₂O₄ composite in contact with molten converter slag[J].Journal of the European Ceramic Society,2023,43(11):5044-5053.
[12] FU L P,HUANG A,GU H Z, et al.Fabrication and characterization of lightweight microporous alumina with guaranteed slag resistance[J].Ceramics International,2016,42(7):8724-8728.
[13] WU H D,LIU X D,LIU X X,et al.Effect of alumina content on the crystal structure,lattice thermal expansion and thermal conductivity of aluminium-rich spinel solid solutions[J].Materials Chemistry and Physics,2022,288:126366.

[1]	李飞, 周辉, 杨枝超, 唐中队, 王正芳, 刘威. 不同成型方式精炼钢包包壁工作衬的蚀损机制研究[J]. 耐火材料, 2024, 58(4): 344-348.
[2]	关昀鹤, 郑丽君, 罗旭东, 牛舒楠. 铁尾矿制备碳化硅多孔陶瓷材料及其性能研究[J]. 耐火材料, 2024, 58(3): 246-250.
[3]	周玉栋, 李世鹏, 王文武, 张一帆, 赵辰啸. 高导热氮化硅陶瓷的制备研究进展[J]. 耐火材料, 2024, 58(3): 270-276.
[4]	秦梦黎, 罗颖, 申自强, 刘梦, 宋杰光, 王慈, 刘强. 莫来石晶须/陶瓷纤维增强堇青石质隔热材料[J]. 耐火材料, 2024, 58(1): 8-12.
[5]	杨宗源, 王景然, 王桐, 张锦化, 韩兵强, 倪月娥, 柯昌明. 不同碱度渣对刚玉-尖晶石浇注料的侵蚀行为研究[J]. 耐火材料, 2024, 58(1): 13-18.
[6]	徐国涛, 王志强, 秦世民, 刘黎, 张洪雷, 张彦文, 周旺枝. 新一代六铝酸钙质浇注料的研制与应用[J]. 耐火材料, 2024, 58(1): 53-56.
[7]	王志强, 徐国涛, 雷中兴, 彭肖仟, 郑吉红, 刘黎, 王心一, 刘毅, 徐炎明. Al₂O₃-MgAl₂O₄复相骨料对刚玉-尖晶石浇注料抗渣性能的影响[J]. 耐火材料, 2024, 58(1): 63-67.
[8]	车连房, 史成龙, 付卫, 蔡国庆, 张晓序. HIsmelt工艺熔融还原炉用耐火材料的抗侵蚀性研究[J]. 耐火材料, 2023, 57(6): 467-472.
[9]	赵宗强, 张洪睿, 陈留刚. 活性MgO和铝酸钙水泥结合刚玉-尖晶石浇注料性能对比[J]. 耐火材料, 2023, 57(6): 528-530.
[10]	张涛, 谭清华, 冯志源, 王晗, 刘鹏程. 稳定剂种类对高纯氧化锆空心球制品性能的影响[J]. 耐火材料, 2023, 57(5): 397-401.
[11]	郭会师, 杨佳麟, 李文凤, 桂阳海, 赵志强, 刘应凡. 铝硅系原料种类对钙长石质隔热耐火材料性能的影响[J]. 耐火材料, 2023, 57(4): 286-290.
[12]	秦红彬, 金锋, 唐世明, 周慧君, 李红霞, 石书冰, 张三华, 程立, 惠先磊. 二铝酸钙加入量对刚玉浇注料性能的影响[J]. 耐火材料, 2023, 57(3): 189-193.
[13]	朱凯, 杨道媛, 王美姣, 杨亮华, 赵祥, 陈俊寰, 原会雨. 直写成型刚玉-莫来石质多孔材料研究[J]. 耐火材料, 2023, 57(3): 200-204.
[14]	潘元帅, 王刚, 冯海霞, 柳军, 田朋丹, 韩艺辉, 王建斌. 结合剂种类对刚玉-尖晶石浇注料抗镍基高温合金侵蚀性能的影响[J]. 耐火材料, 2023, 57(3): 220-225.
[15]	肖雄, 魏耀武, 周辉, 颜林, 陈志强, 邵长波. 富铝尖晶石微粉对刚玉-尖晶石浇注料关键使用性能的影响[J]. 耐火材料, 2022, 56(6): 499-504.

以微孔刚玉-尖晶石骨料替代刚玉骨料制备刚玉-尖晶石浇注料

Preparation of corundum-spinel castables using microporous corundum-spinel aggregates to replace corundum aggregates

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价