耐火材料的MgAlON晶须结合

doi:10.3969/j.issn.1001-1935.2023.05.014

耐火材料 ›› 2023, Vol. 57 ›› Issue (5): 438-441.DOI: 10.3969/j.issn.1001-1935.2023.05.014

耐火材料的MgAlON晶须结合

郭宗奇

西安建筑科技大学材料科学与工程学院陕西西安 710055

收稿日期:2023-07-26 出版日期:2023-10-15 发布日期:2023-10-26
作者简介:郭宗奇:男,1962年生,博士,教授。E-mail: guozongqi@xauat.edu.cn

MgAlON whisker bond in refractories

Guo Zongqi

First author's address: School of Materials Science and Engineering,Xi’an University of Architecture and Technology,Xi’an 710055,Shaanxi,China

Received:2023-07-26 Online:2023-10-15 Published:2023-10-26

摘要/Abstract

摘要： RH脱气炉用无铬化的方镁石-尖晶石-Al不烧砖具有优越的力学特性和抗渣渗透性,在极其苛刻的使用条件下成功取代传统的镁铬砖。与传统的陶瓷结合不同的是,方镁石-尖晶石-Al不烧砖使用后呈现微米级柱状MgAlON晶须相互交织、浓密网状分布的结合基质。为建立和完善晶须结合的概念,归纳了耐火材料中晶须结合的特征,晶须形成的机制和条件,晶须增强和晶须结合的不同之处。

关键词: RH脱气炉, 方镁石-尖晶石-Al不烧砖, MgAlON晶须, 晶须结合

Abstract: Unburned periclase-spinel-Al bricks,as a chromium-free material for RH degassers,have superior mechanical characteristics and slag penetration resistance,successfully replacing traditional magnesia-chrome bricks under extremely harsh working conditions.Instead of the common ceramic bond,a whisker bond is formed in the matrix of used periclase-spinel-Al bricks,which exhibits micron-size columnar MgAlON whiskers and densely interwoven network structure.The concept of the whisker bond was suggested in refractories,by detailing its fundamental characteristics and formation mechanism and differentiating whisker reinforcement and the whisker bond in this article.

Key words: RH degassers, unburned periclase-spinel-Al bricks, MgAlON whiskers, whisker bond

中图分类号:

TQ175

郭宗奇. 耐火材料的MgAlON晶须结合[J]. 耐火材料, 2023, 57(5): 438-441.

Guo Zongqi. MgAlON whisker bond in refractories[J]. Refractories, 2023, 57(5): 438-441.

参考文献

[1] RANDALL M G,PAVAN S,SEONG J P.Review:liquid phase[J].Journal of Materials Science,2009,44:1-39.
[2] GUO Z Q,MA Y,DANG X M,FENG C,et al.Critical whisker bond of a profound chromium-free refractory for RH degassers[J].Sādhanā,2022,47(2):1-10.
[3] GUO Z Q,MA Y,RAINER N, et al.Thermal evolution of Al-containing magnesia refractory for RH snorkels[J].China’s Refractories,2019,28(1):1-6.
[4] GUO Z Q,LEI Z X,MA Y,et al.Bonding phase formation in eco-friendly periclase-spinel-Al bricks used in RH degassing process[J].Journal of the European Ceramic Society,2023,43(6):2663-2674.
[5] GUO Z Q,DAI Y J,CHEN J H,et al.Three bond modes of basic refractories used for Ruhrstahl Heraeus degassing process[J].Journal of the American Ceramic Society,2023,106(9):5403-5419.
[6] KARAMIAN E,MONSHI A.Influence of additives on nano-SiC whisker formation in alumina silicate-SiC-C monolithic refractories[J].Ceramics International,2010,36(2):811-816.
[7] KARAMIAN E,MONSHI A,BATAILLE A,et al.Formation of nano SiC whiskers in bauxite-carbon composite materials and their consequences on strength and density[J].Journal of the European Ceramic Society,2011,31 (14):2677-2685.
[8] ZHU B Q,ZHU Y N,LI X C,et al.Effect of ceramic bonding phases on the thermo-mechanical properties of Al₂O₃-C refractories[J].Ceramics International,2013,39(6):6069-6076.
[9] ATZENHOFER C,HARMUTH H.Phase formation in MgO-C refractories with different antioxidants[J].Journal of the European Ceramic Society,2021,41(14):7330-7338.
[10] WIEDEMANN H G,NERBEL J,RELLER A.Structuring and texturing aluminum oxides[J].Thermochemica Acta,1998,318(1/2):71-82.
[11] YAMAGUCHI A,HASHIMOTO S.Growth of magnesia whiskers[J].Ceramics International,1992,18(5):301-305.
[12] PYZIK A J,HART A M.The use of phase studies in the development of whisker and whisker-reinforced ceramics[M].New York:Academic Press,Inc.,1995.
[13] TELLE R.The role of whisker for the reinforcement of refractories[C]//Proceedings of 55^th International Colloquium on Refractories,Aachen,Germany,2012:199-204.
[14] ANEZIRIS C G,HUBÁLKOVÁ J,BARABÁS R.Microstructure evaluation of MgO-C refractories with TiO₂ and Al additions[J].Journal of the European Ceramic Society,2007,27(1):73-78.
[15] COELLE D,ANEZIRIS C G,SCHAERFL W,et al.Novel alumosilicate-C composites due to nanoparticle additions[C]//Proceedings of the United International Technical Conference on Refractories,Dresden,German,2007:148-151.
[16] MATSUO Y,TANAKA M,YOSHITOMI J,et al.Effect of the carbon nanofiber addition on the mechanical properties of MgO-C bricks[C]// Proceedings of the United International Technical Conference on Refractories,Kyoto,Japan,2011:2-E-12.

耐火材料的MgAlON晶须结合

MgAlON whisker bond in refractories

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	姚路炎, 韩兵强, 张锦化, 柯昌明. Ti-Si-Fe合金添加量对Si₃N₄结合SiC材料结构与性能的影响[J]. 耐火材料, 2024, 58(4): 277-283.
[2]	昝文宇, 马北越, 陈广鑫, 曹长坤, 李孟强. 利用低压电瓷废料和二次铝灰制备莫来石陶瓷基多孔骨料[J]. 耐火材料, 2024, 58(4): 302-306.
[3]	邓江, 刘学新, 李文, 张子翼, 员文杰. 氧化铝粒径和氧化锆粉外加量对氧化铝造粒粉性能的影响[J]. 耐火材料, 2024, 58(4): 307-313.
[4]	李文凤, 申天姿, 郭会师, 曹金金, 康晓旭, 石凯, 康晓阳. 多羟基糖类结合剂对Al₂O₃-SiC-C质无水炮泥性能的影响[J]. 耐火材料, 2024, 58(4): 314-318.
[5]	安佳瑞, 张锐, 范冰冰, 王刚, 杜鹏辉. Sm₂O₃加入量和热处理温度对CA₆-MA材料性能的影响[J]. 耐火材料, 2024, 58(4): 319-322.
[6]	李莹, 汪涤, 赵莉, 尹艺程, 贾全利. 石墨类型对Al₂O₃-MgO浇注料性能的影响[J]. 耐火材料, 2024, 58(4): 323-328.
[7]	凌厦厦, 相宇博, 郑翰, 吴吉光. 酚醛/环氧树脂凝胶注模成型制备反应烧结碳化硅[J]. 耐火材料, 2024, 58(4): 329-333.
[8]	李飞, 周辉, 杨枝超, 唐中队, 王正芳, 刘威. 不同成型方式精炼钢包包壁工作衬的蚀损机制研究[J]. 耐火材料, 2024, 58(4): 344-348.
[9]	李坤鹏, 闫双志, 张涛, 石鹏坤, 冯志源, 范沐旭, 王晗, 刘鹏程. 回转窑炉渣对刚玉-莫来石砖的侵蚀研究[J]. 耐火材料, 2024, 58(4): 349-353.
[10]	徐晓莹, 曹海洁, 魏立超, 马旭峰. 能量色散X射线荧光光谱仪在镁砂成分测定中的应用[J]. 耐火材料, 2024, 58(4): 354-356.
[11]	游杰刚, 赵鑫, 钱国华, 张小芳, 张国栋, 马北越. 辽南地区电熔镁砂的发展现状[J]. 耐火材料, 2024, 58(4): 357-361.
[12]	谭栖桐, 赵惠忠, 余俊, 张寒, 谈利强. 固废资源合成堇青石工艺及其性能研究[J]. 耐火材料, 2024, 58(3): 185-189.
[13]	王昕悦, 许晴, 朱欣欣, 周瑞琪, 段红娟, 张海军, 李少平. 固相反应合成MgAl₂O₄多孔纤维的研究[J]. 耐火材料, 2024, 58(3): 190-194.
[14]	程旭, 邓承继, 董博, 邹起良, 丁军, 王周福, 朱万政, 肖语嫣, 祝洪喜, 余超. Y₂O₃对氧化物结合Ti(C,N)复合材料性能的影响[J]. 耐火材料, 2024, 58(3): 195-198.
[15]	刘中飞, 吴锋, 李心慰, 梁效诚, 罗旭东, 钱国华. CaO对MgAl₂O₄材料和ZrO₂-MgAl₂O₄材料侵蚀机制研究[J]. 耐火材料, 2024, 58(3): 199-203.