连铸用浸入式水口防结瘤研究进展

doi:10.3969/j.issn.1001-1935.2021.06.017

耐火材料 ›› 2021, Vol. 55 ›› Issue (6): 533-538.DOI: 10.3969/j.issn.1001-1935.2021.06.017

连铸用浸入式水口防结瘤研究进展

刘国齐¹^,³⁾(), 李红霞¹^,³⁾, 袁磊²⁾, 杨文刚¹^,³⁾, 钱凡¹^,³⁾, 马渭奎¹^,³⁾, 于建宾¹^,³⁾, 顾强¹^,³⁾, 于景坤²⁾

1)中钢集团洛阳耐火材料研究院有限公司先进耐火材料国家重点实验室　河南洛阳 471039
2)东北大学　辽宁沈阳 110819
3)有色金属新材料与先进加工技术省部共建协同创新中心　河南洛阳 471023

收稿日期:2020-11-18 出版日期:2021-12-15 发布日期:2021-12-10
作者简介:刘国齐:男,1975年生,博士,教授级高级工程师。E-mail: liugq@lirrc.com
基金资助:
国家自然科学基金资助项目(51932008);国家自然科学基金资助项目(51772277);中原科技创新领军人才资助项目(204200510011)

Research progress on anti-clogging technology of submerged entry nozzle for continuous casting

Liu Guoqi¹^,³⁾(), Li Hongxia¹^,³⁾, Yuan Lei²⁾, Yang Wengang¹^,³⁾, Qian Fan¹^,³⁾, Ma Weikui¹^,³⁾, Yu Jianbin¹^,³⁾, Gu Qiang¹^,³⁾, Yu Jingkun²⁾

1) State Key Laboratory of Advanced Refractories,Sinosteel Luoyang Institute of Refractories Research Co.,Ltd.,Luoyang 471039,Henan,China

Received:2020-11-18 Online:2021-12-15 Published:2021-12-10

摘要/Abstract

摘要：

介绍了水口结瘤产生的原因、结瘤物的形成过程、防止水口结瘤的方法,重点综述了电场对浸入式水口结瘤的影响,包括浸入式水口荷电的基础理论和测量、浸入式水口荷电初步研究、电场条件下钢液对耐火材料润湿行为的影响、电场对熔融金属中的氧化物夹杂的影响。基于流体力学、化学等因素对耐火材料材质、结构及夹杂物颗粒传递、黏附的影响规律,通过优化工艺条件、内壁复合防堵塞材料、创新浸入式水口结构、施加物理场等开展了较多的研究,使水口结瘤问题得到了一定程度的解决,但适用性不强、结瘤机制研究不深入等问题仍然很突出;利用电场调控防止浸入式水口结瘤堵塞作为一种新兴的防堵技术,虽然已在连铸现场试验中取得了一定的效果,但施加电场方式、电场参数及设备等工艺问题还需逐步完善,对夹杂物、浸入式水口材料在高温下的表面特性还需进一步深入研究。最后指出材料与外加电场结合将成为浸入式水口防堵塞技术的重要方向。

关键词: 连铸, 浸入式水口, 夹杂物, 结瘤, 堵塞, 电场

Abstract:

The causes,the formation process,and the prevention of submerged entry nozzle (SEN) clogging were introduced.The influence of electric field on the SEN clogging was focused on,including the basic theory and measurement of SEN charging,the preliminary research on SEN charging,the influence of molten steel on the wetting behavior of refractory materials in electric field,and the influence of electric field on the oxide inclusions in molten steel.Based on the influence of the hydrodynamics,chemistry and other factors on refractory materials,structure,inclusion particle transfer and adhesion,many anti-clogging researches have been carried out,such as optimizing process conditions,compositing anti-clogging inner lining materials,innovating SEN structure and applying physical fields,which solve the problem of SEN clogging to a certain extent.However,the problems of weak adaptability and superficial study on clogging mechanism are still prominent.The electric field control is a new technology to prevent clogging.Although it has achieved certain results in on-site continuous casting trials,some problems such as the method of applying electric field,the electric field parameters and the equipment still need to be gradually improved,and the surface characteristics of inclusions and SEN materials at high temperatures need to be further studied.It was pointed out that the combination of materials and applied electric field will become an important direction for SEN anti-clogging technology.

Key words: continuous casting, submerged entry nozzle, inclusions, clogging, blocking, electric field

中图分类号:

TQ175

刘国齐, 李红霞, 袁磊, 杨文刚, 钱凡, 马渭奎, 于建宾, 顾强, 于景坤. 连铸用浸入式水口防结瘤研究进展[J]. 耐火材料, 2021, 55(6): 533-538.

Liu Guoqi, Li Hongxia, Yuan Lei, Yang Wengang, Qian Fan, Ma Weikui, Yu Jianbin, Gu Qiang, Yu Jingkun. Research progress on anti-clogging technology of submerged entry nozzle for continuous casting[J]. Refractories, 2021, 55(6): 533-538.

图/表 3

参考文献 47

[1]	李红霞, 刘国齐, 杨彬, 等. 连铸用功能耐火材料的发展[J]. 耐火材料, 2001, 35(1):45-49.
[2]	KOJOLA N, EKEROT S, ANDERSSON M, et al. Pilot plant study of nozzle clogging mechanisms during casting of REM treated stainless steels[J]. Ironmaking & Steelmaking, 2011, 38(1):1-11.
[3]	SUN M K, JUNG I H, LEE H G. Morphology and chemistry of oxide inclusions after Al and Ti complex deoxidation[J]. Metals & Materials International, 2008, 14(6):791.
[4]	BASU S, CHOUDHARY S K, GIRASE N U. Nozzle clogging behaviour of Ti-bearing Al-killed ultra low carbon steel[J]. ISIJ International, 2004, 44(10):1653-1660. DOI URL
[5]	ZHANG L F, WANG Y F, ZUO X J. Flow transport and inclusion motion in steel continuous-casting mold under submerged entry nozzle clogging condition[J]. Metallurgical and Materials Transactions B, 2008, 39(4):534-550. DOI URL
[6]	VERMEULEN Y, COLETTI B, WOLLANTS P, et al. Clogging in submerged entry nozzles.Steel research[J]. 2000, 71(10):391-395.
[7]	RACKERS K, THOMAS B G. Clogging in continuous casting nozzles[C]//78^th Steelmaking Conference Proceedings,Nashville,US, 1995:723-734.
[8]	吴苏州, 张炯明. 连铸浸入式水口结瘤现象的研究现状及发展[J]. 钢铁研究学报, 2007, 19(12):1-4.
[9]	王睿之, 杨健, 职建军, 等. 连铸中间包上水口及浸入式水口结瘤物分析[J]. 宝钢技术, 2012 (5):13-16.
[10]	WANG Y, SRIDHAR S, VALDEZ M. Formation of CaS on Al₂O₃-CaO inclusions during solidification of steels[J]. Metallurgical & Materials Transactions B, 2002, 33(4):625-632.
[11]	乔焕山, 王莉, 陈玉鑫, 等. 浅析连铸铝镇静钢水口结瘤问题[C]//第十八届(2014年)全国炼钢学术会议论文集,西安, 2014:313-320.
[12]	DEKKERS R, BLANPAIN B, WOLLANTS P, et al. A morphological comparison between inclusions in aluminium killed steels and deposits in submerged entry nozzle[J]. Steel Research International, 2003, 74(6):351-355. DOI URL
[13]	TEHOVNIK F, BURJA J, ARH B, et al. Submerged entry nozzle clogging during continuous casting of Al-killed steel[J]. Metallurgy, 2015, 54(2):371-374.
[14]	SAMBASIVAM R. Clogging resistant submerged entry nozzle design through mathematical modelling[J]. Ironmaking & Steelmaking, 2006, 33(6):439-453.
[15]	赵定国, 李新, 王书桓, 等. 钢水中夹杂物与耐火材料的反应吸附行为[J]. 钢铁, 2016, 51(6):47-52.
[16]	UEMURA K I, TAKAHASHI M, KOYAMA S, et al. Filtration mechanism of non-metallic inclusions in steel by ceramic loop filter[J]. ISIJ International, 1992, 32(1):150-156. DOI URL
[17]	NADIF M, LEHMANN J, BURTY M, et al. Control of steel reoxidation and cc nozzle clogging:an overview[J]. Revue de Métallurgie, 2007, 104(10):493-500. DOI URL
[18]	DENG Z Y, ZHU M Y, ZHONG B J, et al. Attachment of liquid calcium aluminate inclusions on inner wall of submerged entry nozzle during continuous casting of calcium-treated steel[J]. ISIJ International, 2014, 54(12):2813-2820. DOI URL
[19]	TSUJINO R, TANAKA A, IMAMURA A, et al. Mechanism of deposition of inclusion and metal in ZrO₂-CaO-C immersion nozzle of continuous casting[J]. ISIJ International, 1994, 34(11):853-858. DOI URL
[20]	YANG B, LI H X, LIU G Q, et al. Study on anti-clogging SEN for special alloy steel continuous casting[C]//Proc of UNITECR’05,Orlando,US, 2005:758-761.
[21]	VERMEULEN Y, COLETTI B, BLANPAIN B, et al. Material evaluation to prevent nozzle clogging during continuous casting of al killed steels[J]. ISIJ International, 2002, 42(11):1234-1240. DOI URL
[22]	PRASAD B, SAHU J K, TIWARI J N. Design and development of anti-clogging nozzles for casting of aluminium killed steel[C]//Proc of UNITECR’07,Dresden,German, 2007:208-211.
[23]	加知岳志, 高橋成彰, 山内智玲. 連続鋳造用浸漬ノズルにおける難付着材質の開発[J]. 耐火物, 2018, 70(6):269-275.
[24]	SVENSSON J K S, MEMARPOUR A, EKEROT S, et al .Studies of new coating materials to prevent clogging of submerged entry nozzle (sen) during continuous casting of al killed low carbon steels[J]. Ironmaking & Steelmaking, 2017, 44(2):117-127.
[25]	TUTTLE R B, SMITH J D, PEASLEE K D. Casting simulation of calcium titanate and calcium zirconate nozzles for continuous casting of aluminum-killed steels[J]. Metallurgical and Materials Transactions B, 2007, 38(1):101-108. DOI URL
[26]	TSUKAGUCHI Y, HAYASHI H, KURIMOTO H, et al. Development of swirling-flow submerged entry nozzles for slab casting[J]. ISIJ International, 2010, 50(5):721-729. DOI URL
[27]	苏志坚, 李德伟, 丸川雄净, 等. 电磁旋流水口在钢圆坯连铸中的作用[J]. 连铸, 2011(增刊):183-188.
[28]	OSAMU N, SHINSUKE I, MASANORI O. Water model simulation of “mogul-lined” submerged entry nozzle. Taikabutsu Overseas, 2004, 24(3):194-197.
[29]	YANG Y, JÖNSSON P G, ERSSON M, et al. Inclusion behavior under a swirl flow in a submerged entry nozzle and mold[J]. Steel Research International, 2015, 86(4):341-360. DOI URL
[30]	YU J K, YANG X, LIU Z Y, et al. Anti-clogging of submerged entry nozzle through control of electrical characteristics[J]. Ceramics International, 2017, 43(15):13025-13029. DOI URL
[31]	CAO X, JIE Y, WANG N, et al. Triboelectric nanogenerators driven self-powered electrochemical processes for energy and environmental science[J]. Advanced Energy Materials, 2016, 6(23):1600665. DOI URL
[32]	LOWELL J, TRUSCOTT W S. Triboelectrification of identical insulators Ⅱ:Theory and further experiments[J]. Journal of Physics D:Applied Physics, 1986, 19(7):1281-1298. DOI URL
[33]	陈肇友, 张欣, 杨丁熬, 等. 含碳耐火材料的电化学侵蚀[J]. 硅酸盐学报, 1991(5):442-447.
[34]	PAIK Y H, YOON W J, SHIN H C. Static electrification of solid oxide in liquid metal and electrical double layer at the interface[J]. Journal of Colloid Interface Science, 2004, 269(2):354-357. DOI URL
[35]	HOU X H, YU J K, SHENG M K, et al. Influencing factors to the friction charging in water delivery metal pipeline[J]. Journal of Electrostatics, 2016, 82:7-10. DOI URL
[36]	ZHU S X, LIU L, TAKAHASHI S. Flow electrification of insulated liquid in metal pipes[J]. Chinese Journal of Mechanical Engineering, 2012, 25(6):1115-1120. DOI URL
[37]	田强, 周绍骑, 刘凯, 等. 流速对管输油品静电的影响[J]. 油气储运, 2013, 32(2):203-206+222.
[38]	YANG X, YU J K, LIU Z Y, et al. The charged characteristics of the submerged entry nozzle used for continuous casting[J]. Ceramics International, 2017, 43(2):2881-2883. DOI URL
[39]	HEIKKINEN E P, MATTILA R, KOKKONEN T M T, et al. The chemical wear of the SEN-slagline in the continuous casting of stainless steels[C]//85^th Steelmaking Conference,Nashville,US, 2002:419-428.
[40]	LEE Y M, YIN H. Zirconia graphite wear and steel inclusions [C]//49^th Annual Conference of Metallurgists,Vancouver,Canada, 2010:221-230.
[41]	LI X M, TIAN H M, SHAO J Y, et al. Decreasing the saturated contact angle in electrowetting-on-dielectrics by controlling the charge trapping at liquid-solid interfaces[J]. Advanced Functional Materials, 2016, 26(18):2994-3002. DOI URL
[42]	KIM J H, LEE J M, SHIN H C, et al. Separation of oxide inclusions from liquid metal in an applied electrostatic field[J]. Metals and Materials International, 2003, 9(6):593-597. DOI URL
[43]	DAI W B, YU J K, DU C M, et al. Refinement of inclusions in molten steel by electric current pulse[J]. Materials Science and Technology, 2015, 31(13):1555-1559. DOI URL
[44]	DAI W B, ZHOU X L, YANG X, et al. Formation of dense inclusion buildup on submerged entry nozzle by electric current pulse[J]. Acta Metallurgica Sinica(English Letters), 2016, 29(5):500-504.
[45]	MIKI Y, KITAOKA H, SAKURAYA T, et al. Mechanism for separating inclusions from molten steel stirred with a rotating electro-magnetic field[J]. ISIJ International, 1992, 32(1):142-149. DOI URL
[46]	SASAI K. Direct measurement of agglomeration force exerted between alumina particles in molten steel[J]. ISIJ International. 2014, 54(12):2780-2789. DOI URL
[47]	MATSUSAKA S, GHADIRI M, MASUDA H. Electrification of an elastic sphere by repeated impacts on a metal plate[J]. Journal of Physics D:Applied Physics, 2000, 33(18):2311-2319. DOI URL

连铸用浸入式水口防结瘤研究进展

Research progress on anti-clogging technology of submerged entry nozzle for continuous casting

RichHTML

PDF

可视化

摘要/Abstract

引用本文

使用本文

图/表 3

参考文献 47

相关文章 15

编辑推荐

Metrics

本文评价

[1]	田晨, 职建军, 甘菲芳, 范正洁, 高华, 袁磊, 刘国齐, 于景坤, 李红霞. ZrO₂-C质浸入式水口渣线耐火材料的侵蚀机制分析[J]. 耐火材料, 2023, 57(2): 113-116.
[2]	李延, 袁磊, 田晨, 刘国齐, 于景坤, 李红霞. 脉冲电场对浸入式水口渣线耐火材料侵蚀的影响[J]. 耐火材料, 2022, 56(5): 374-379.
[3]	沈明科, 罗明, 胡承洋, 喻燕, 宋雅楠, 倪飞江, 李金. 四种不同氧化铝微粉对Al₂O₃-C材料性能的影响[J]. 耐火材料, 2021, 55(6): 498-501.
[4]	曹磊, 石永亮, 马保振, 黄伟青, 韩立浩. TRIZ理论在改善引流砂对钢液危害中的应用[J]. 耐火材料, 2021, 55(6): 517-521.
[5]	杨全海, 王重君, 白晓卫, 杨晓乐, 丁宁, 罗诚. 长寿命板坯中间包的生产实践[J]. 耐火材料, 2021, 55(6): 522-524.
[6]	孙亚东, 杜传明, 袁磊, 于景坤. 利用外加电流抑制浸入式水口堵塞的研究进展[J]. 耐火材料, 2021, 55(4): 364-368.
[7]	闪静祎, 王军凯, 黄珍霞, 戴新宇, 胡前库, 周爱国. 外电场对水在CaO(100)表面吸附的第一性原理计算[J]. 耐火材料, 2021, 55(1): 44-50.
[8]	徐国涛1),刘孟1),吴杰1),张彦文2) ,张洪雷1). 连铸中间包涂料组成及性能对钢水增氢的影响分析[J]. , 2020, 54(4): 361-364.
[9]	魏昌晟1,2), 雷贤卿1), 曹喜营2）, 闫广周2). TRIZ创新方法在浸入式水口成型工艺改进中的应用[J]. , 2020, 54(2): 152-155.
[10]	唐冰杰1),王梓祎1),李金雨1, 2),连伟康1, 2),涂军波1),魏军从1),刘永辉1). PVP结合镁质中间包干式料的研制[J]. , 2019, 53(3): 211-213.
[11]	郁书中1),彭学峰1),崔任渠1),刘正龙2),邓承继2). 含不烧镁橄榄石的镁质中间包涂料对汽车板钢洁净度的影响[J]. , 2019, 53(2): 101-105.
[12]	闫广周,钱凡,杨文刚,刘国齐. 不同添加剂对镁碳质水口材料性能的影响[J]. , 2018, 52(2): 135-139.
[13]	杨时标1）,金从进2）. 连铸功能耐火材料制造的造粒工艺[J]. , 2017, 51(4): 317-320.
[14]	魏昌晟1,2)刘国齐2)闫广周2)王建国2). 连铸“三大件”冷等静压成型工艺仿真[J]. , 2017, 51(1): 44-46.
[15]	孟红涛,王允,郝明选. 机压弥散型中间包镁质气幕挡墙的研制及应用[J]. , 2016, 50(1): 67-68.