活性氧化铝加入量对活性氧化镁结合刚玉-尖晶石浇注料性能的影响

doi:10.3969/j.issn.1001-1935.2024.05.010

耐火材料 ›› 2024, Vol. 58 ›› Issue (5): 419-423.DOI: 10.3969/j.issn.1001-1935.2024.05.010

活性氧化铝加入量对活性氧化镁结合刚玉-尖晶石浇注料性能的影响

高广泽¹⁾, 张洪睿¹⁾, 李建伟²⁾, 陈留刚¹⁾

1)郑州大学材料科学与工程学院河南省高温功能材料重点实验室河南郑州 450052
2)河南建筑材料研究设计院有限责任公司河南郑州 450002

收稿日期:2024-01-29 出版日期:2024-10-15 发布日期:2024-10-16
作者简介:高广泽:男,2000年生,硕士研究生。E-mail:gzgao@gs.zzu.edu.cn
基金资助:
郑州市协同创新重大专项(20XTZX12025)和河南省优势学科联合基金培育项目(222301420034)。

Effect of reactive alumina addition on properties of activated magnesia bonded corundum-spinel castables

Gao Guangze, Zhang Hongrui, Li Jianwei, Chen Liugang

Henan Key Laboratory of High Temperature Functional Ceramics,School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450052,Henan,China

Received:2024-01-29 Online:2024-10-15 Published:2024-10-16

摘要/Abstract

摘要： 为改善活性氧化镁结合刚玉-尖晶石浇注料的性能,以板状刚玉、活性氧化铝微粉、活性氧化镁微粉和乳酸铝为原料,制备了活性氧化镁结合刚玉-尖晶石浇注料,研究了活性氧化铝微粉加入量(加入质量分数分别为0、8%、13%和18%)对浇注料显微结构、物相组成、物理性能及抗渣侵蚀和渗透性能的影响。结果表明:1)活性氧化铝微粉的加入促进了活性氧化镁结合刚玉-尖晶石浇注料的烧结,提高了骨料和基质的结合程度,使浇注料显微结构更加致密;2)随着活性氧化铝微粉加入量的增加,试样体积稳定性提高,显气孔率降低,体积密度增加,常温抗折强度和耐压强度及抗渣性提高;3)当活性氧化铝微粉加入量为18%(w)时,活性氧化镁结合刚玉-尖晶石浇注料的综合性能最好(考虑到颗粒级配和原料成本的问题,没有必要再进一步增加活性氧化铝微粉),其体积密度为3.05 g·cm^-3,显气孔率为18.5%,加热永久线变化为0.31%,常温抗折强度和耐压强度分别为13.5和73.8 MPa,抗渣性最佳。

关键词: 活性氧化铝微粉, 活性氧化镁, 刚玉-尖晶石浇注料, 物理性能, 抗渣性

Abstract: To enhance their performance,reactive MgO-bonded corundum-spinel castables were prepared using tabular corundum,reactive alumina,reactive MgO and aluminum lactate as raw materials.The influence of the reactive alumina addition (0,8%,13% and 18%,by mass) on the microstructure,phase composition,physical properties,as well as the resistance to slag corrosion and penetration of the castables was investigated.The results reveal that:(1)the reactive alumina promotes the sintering of the reactive MgO-bonded corundum-spinel castables,enhancing the bonding between aggregates and matrix,thus densifying the microstructure;(2)with the increase of the reactive alumina addition,the volume stability of the samples increases,the apparent porosity decreases,the bulk density increases,and the cold modulus of rupture and cold crushing strength as well as the slag resistance are improved;(3)the reactive MgO-bonded corundum-spinel castable with 18% reactive alumina shows optimal comprehensive performance,with the bulk density of 3.05 g·cm^-3,apparent porosity of 18.5%,permanent linear change rate after heating of 0.31%,cold modulus of rupture of 13.5 MPa and cold compressive strength of 73.8 MPa,as well as the best slag resistance.However,considering particle size distribution and raw material costs,there is no need to further increase the reactive alumina addition.

Key words: reactive alumina micropowder, reactive magnesia, corundum-spinel castables, physical properties, slag resistance

中图分类号:

TQ175

高广泽, 张洪睿, 李建伟, 陈留刚. 活性氧化铝加入量对活性氧化镁结合刚玉-尖晶石浇注料性能的影响[J]. 耐火材料, 2024, 58(5): 419-423.

Gao Guangze, Zhang Hongrui, Li Jianwei, Chen Liugang. Effect of reactive alumina addition on properties of activated magnesia bonded corundum-spinel castables[J]. Refractories, 2024, 58(5): 419-423.

参考文献

[1] 王恩会,陈俊红,侯新梅.钢包工作衬用耐火材料的研究现状及最新进展[J].工程科学学报,2019,41(6):695-708.
[2] 张艳利,彭西高,程庆先.连铸钢包及炉外精炼钢包用耐材技术的研究与发展[J].耐火与石灰,2023,48(6):5-17.
[3] 张艳利,汪涤,李莹,等.耐火浇注料结合体系的优化与研究进展[J].耐火材料,2021,55(6):539-544.
[4] LUZ A P,CONSONI L B,PAGLIOSA C,et al. MgO fumes as a potential binder for in situ spinel containing refractory castables[J].Ceramics International,2018,44(13):15453-15463.
[5] GUO L,SONG S Q,MU Y D,et al.Inhibited Cr(VI) formation in Cr₂O₃-containing refractory castable using reactive MgO as hydraulic binder[J].Journal of the European Ceramic Society,2022,42(16):7656-7666.
[6] SHEN W G,CAO L,LI Q,et al.Is magnesia cement low carbon?Life cycle carbon footprint comparing with Portland cement[J].Journal of Cleaner Production,2016,131:20-27.
[7] ZAHNG H R,CHEN L G,GAO G Z,et al.Microstructure,mechanical property and slag corrosion resistance of (Al,Cr)₂O₃-Mg(Al,Cr)₂O₄-Ca(Al,Cr)₁₂O₁₉ composite refractory using alumina-chromia slag[J].Journal of the European Ceramic Society,2024,44(1):557-566.
[8] ZHANG H R,WANG M Q,JIA Q L,et al.Corrosion mechanism of reactive MgO-bonded Cr₂O₃-bearing castables in CaO-Al₂O₃-Fe₂O₃-SiO₂-based steel-making slag[J].Journal of the American Ceramic Society,2024,107(2):1232-1248.
[9] 赵宗强,张洪睿,陈留刚.活性MgO和铝酸钙水泥结合刚玉-尖晶石浇注料性能对比[J].耐火材料,2023,57(6):528-530+537.
[10] ZHANG H R,ZHAO Z Q,XIAO J T,et al.Particle grading effect on properties of reactive MgO-bonded castables[J].International Journal of Applied Ceramic Technology,2024,24(1):590-597.
[11] 沈明科,罗明,胡承洋,等.四种不同氧化铝微粉对Al₂O₃-C材料性能的影响[J].耐火材料,2021,55(6):498-501.
[12] 李仕祺,李远兵,魏昊,等.活性氧化铝微粉种类对钢包用ρ-Al₂O₃结合Al₂O₃-MgO浇注料性能的影响[J].耐火材料,2020,54(5):399-403+408.
[13] WANG S Y,ZHANG L,HUANG M,et al.Effects of different additives on properties of magnesium aluminate Spinel-Periclase castable[J].Ceramics International,2023,49(3):4212-4221.
[14] 唐海,石颖恒,员文杰.活性氧化铝微粉对刚玉质浇注料性能的影响[J].耐火材料,2022,56(5):423-426.
[15] 白晨,邓承继,李享成.氧化铝微粉对刚玉浇注料高温性能的影响[J].硅酸盐学报,2018,46(9):1315-1320.
[16] BORGES O H,SARDELLI J A P,PAGLIOSA NETO C,et al.ZnO and MgO as inducers of spinel-like phase formation on alumina-based castables[J].Journal of the European Ceramic Society,2022,42(15):7335-7342.

活性氧化铝加入量对活性氧化镁结合刚玉-尖晶石浇注料性能的影响

Effect of reactive alumina addition on properties of activated magnesia bonded corundum-spinel castables

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁效诚, 冯雨, 刘中飞, 罗旭东, 黄敏, 吴锋. 预合成CaZrO₃对镁锆质耐火材料性能的影响[J]. 耐火材料, 2024, 58(3): 213-217.
[2]	何维祥, 罗明, 何亮, 柯极峰. 高精炼比模式下钢包渣线镁碳砖的研制及应用[J]. 耐火材料, 2024, 58(3): 234-237.
[3]	鞠茂奇, 马骁一, 程水明, 夏昌勇, 魏建修, 张晓存, 单江博, 高东升. 用后铁沟料加入量对Al₂O₃-SiC-C质浇注料性能的影响[J]. 耐火材料, 2024, 58(3): 238-241.
[4]	刘中飞, 冯雨, 梁效诚, 罗旭东, 李广伟, 吴锋. 预合成镁锆砂和煅烧温度对镁锆质材料性能的影响[J]. 耐火材料, 2024, 58(2): 110-115.
[5]	杨宗源, 王景然, 王桐, 张锦化, 韩兵强, 倪月娥, 柯昌明. 不同碱度渣对刚玉-尖晶石浇注料的侵蚀行为研究[J]. 耐火材料, 2024, 58(1): 13-18.
[6]	王志强, 徐国涛, 雷中兴, 彭肖仟, 郑吉红, 刘黎, 王心一, 刘毅, 徐炎明. Al₂O₃-MgAl₂O₄复相骨料对刚玉-尖晶石浇注料抗渣性能的影响[J]. 耐火材料, 2024, 58(1): 63-67.
[7]	鞠茂奇, 程水明, 夏昌勇, 梁永和, 丛培源, 聂建华. 锂离子电池正极材料用莫来石溶胶结合匣钵材料的性能研究[J]. 耐火材料, 2023, 57(6): 495-499.
[8]	刘学新, 张锦化, 陈鑫铭, 王景然, 杨宗源, 韩兵强, 柯昌明. 以微孔刚玉-尖晶石骨料替代刚玉骨料制备刚玉-尖晶石浇注料[J]. 耐火材料, 2023, 57(6): 514-517.
[9]	石干, 范沐旭, 刘新彧. 固溶反应对MA-Al₂O₃材料结构和性能的影响[J]. 耐火材料, 2023, 57(5): 386-389.
[10]	韩艺辉, 曹喜营, 冯海霞, 王晖, 柳军, 潘元帅, 王建斌. 不同结合剂结合MgO-C耐火材料的性能研究[J]. 耐火材料, 2023, 57(5): 402-406.
[11]	贺远航, 钱凡, 郭海荣, 李化龙, 路跃, 刘国齐, 李红霞. h-BN在耐火材料和冶金用高温陶瓷中的应用进展[J]. 耐火材料, 2023, 57(4): 360-364.
[12]	潘元帅, 王刚, 冯海霞, 柳军, 田朋丹, 韩艺辉, 王建斌. 结合剂种类对刚玉-尖晶石浇注料抗镍基高温合金侵蚀性能的影响[J]. 耐火材料, 2023, 57(3): 220-225.
[13]	肖雄, 魏耀武, 周辉, 颜林, 陈志强, 邵长波. 富铝尖晶石微粉对刚玉-尖晶石浇注料关键使用性能的影响[J]. 耐火材料, 2022, 56(6): 499-504.
[14]	唐海, 石颖恒, 员文杰. 活性氧化铝微粉对刚玉质浇注料性能的影响[J]. 耐火材料, 2022, 56(5): 423-426.
[15]	李有奇, 何健, 张嘉良, 李天罡, 吕戌生, 李正坤. 烧结刚玉骨料致密度对刚玉-尖晶石浇注料性能的影响[J]. 耐火材料, 2022, 56(3): 222-225.